data_7008977
loop_
_publ_author_name
'Johansson, Anders'
'Roman, Magnus'
'Seisenbaeva, Gulaim A.'
'Kloo, Lars'
'Szabo, Zoltan'
'Kessler, Vadim G.'
_publ_section_title
;
 The solution thermolysis approach to molybdenum(V) alkoxides:
 synthesis, solid state and solution structures of the bimetallic
 alkoxides of molybdenum(V) and niobium(V), tantalum(V) and
 tungsten(VI)
;
_journal_issue                   3
_journal_name_full
'Journal of the Chemical Society, Dalton Transactions'
_journal_page_first              387
_journal_paper_doi               10.1039/a907720k
_journal_year                    2000
_chemical_formula_moiety         'C30 H70 Mo3 O18 Ta2'
_chemical_formula_sum            'C30 H70 Mo3 O18 Ta2'
_chemical_formula_weight         1368.58
_chemical_name_systematic        trimolybdenumditantalumoctaoxodecaisopropoxide
_space_group_IT_number           61
_symmetry_cell_setting           orthorhombic
_symmetry_space_group_name_Hall  '-P 2ac 2ab'
_symmetry_space_group_name_H-M   'P b c a'
_atom_sites_solution_hydrogens   geom
_atom_sites_solution_primary     direct
_atom_sites_solution_secondary   difmap
_audit_creation_method           SHELXL-97
_cell_angle_alpha                90.00
_cell_angle_beta                 90.00
_cell_angle_gamma                90.00
_cell_formula_units_Z            8
_cell_length_a                   18.8123(11)
_cell_length_b                   18.5541(11)
_cell_length_c                   29.0517(18)
_cell_measurement_reflns_used    '999 with I>10sigma(I) '
_cell_measurement_temperature    293(2)
_cell_measurement_theta_max      28.43
_cell_measurement_theta_min      1.40
_cell_volume                     10140.4(11)
_computing_cell_refinement       ' Bruker SMART '
_computing_data_collection       'Bruker SMART '
_computing_data_reduction        'Bruker SAINTPLUS '
_computing_molecular_graphics    'SHELXTL 5.3 '
_computing_publication_material  'SHELXTL 5.3'
_computing_structure_refinement  'SHELXL-97 (Sheldrick, 1997)'
_computing_structure_solution    'SHELXS-97 (Sheldrick, 1990)'
_diffrn_ambient_temperature      295(2)
_diffrn_measured_fraction_theta_full 0.934
_diffrn_measured_fraction_theta_max 0.934
_diffrn_measurement_device_type  ' SMART CCD 1K '
_diffrn_measurement_method       ' Bruker SMART '
_diffrn_radiation_monochromator  graphite
_diffrn_radiation_source         'fine-focus sealed tube'
_diffrn_radiation_type           MoK\a
_diffrn_radiation_wavelength     0.71073
_diffrn_reflns_av_R_equivalents  0.0677
_diffrn_reflns_av_sigmaI/netI    0.0716
_diffrn_reflns_limit_h_max       22
_diffrn_reflns_limit_h_min       -24
_diffrn_reflns_limit_k_max       18
_diffrn_reflns_limit_k_min       -24
_diffrn_reflns_limit_l_max       35
_diffrn_reflns_limit_l_min       -38
_diffrn_reflns_number            47702
_diffrn_reflns_theta_full        28.43
_diffrn_reflns_theta_max         28.43
_diffrn_reflns_theta_min         1.40
_exptl_absorpt_coefficient_mu    5.079
_exptl_absorpt_correction_T_max  0.1856
_exptl_absorpt_correction_T_min  0.1063
_exptl_absorpt_correction_type   'Bruker SADABS '
_exptl_crystal_colour            orange
_exptl_crystal_density_diffrn    1.793
_exptl_crystal_density_meas      ?
_exptl_crystal_density_method    .
_exptl_crystal_description       prism
_exptl_crystal_F_000             5328
_exptl_crystal_size_max          0.8
_exptl_crystal_size_mid          0.6
_exptl_crystal_size_min          0.5
_refine_diff_density_max         0.966
_refine_diff_density_min         -0.631
_refine_diff_density_rms         0.123
_refine_ls_extinction_method     none
_refine_ls_goodness_of_fit_ref   0.906
_refine_ls_hydrogen_treatment    mixed
_refine_ls_matrix_type           full
_refine_ls_number_parameters     476
_refine_ls_number_reflns         11928
_refine_ls_number_restraints     0
_refine_ls_restrained_S_all      0.906
_refine_ls_R_factor_all          0.1450
_refine_ls_R_factor_gt           0.0507
_refine_ls_shift/su_max          3.460
_refine_ls_shift/su_mean         0.278
_refine_ls_structure_factor_coef Fsqd
_refine_ls_weighting_details
'calc w=1/[σ²(Fo²)+(0.0777P)²+0.0000P] where P=(Fo²+2Fc²)/3'
_refine_ls_weighting_scheme      calc
_refine_ls_wR_factor_gt          0.1161
_refine_ls_wR_factor_ref         0.1535
_reflns_number_gt                5189
_reflns_number_total             11928
_reflns_threshold_expression     >2sigma(I)
_cod_data_source_file            a907720k.txt
_cod_data_source_block           mo3ta2m
_cod_depositor_comments
;
The following automatic conversions were performed:
'_symmetry_cell_setting' value 'Orthorhombic' changed to 'orthorhombic'
according to '/home/saulius/struct/CIF-dictionaries/cif_core.dic'
dictionary named 'cif_core.dic' version 2.4.1 from 2010-06-29.

Automatic conversion script
Id: cif_fix_enum 1527 2010-12-29 10:47:43Z saulius 
;
_cod_original_sg_symbol_H-M      Pbca
_cod_database_code               7008977
loop_
_symmetry_equiv_pos_as_xyz
'x, y, z'
'-x+1/2, -y, z+1/2'
'-x, y+1/2, -z+1/2'
'x+1/2, -y+1/2, -z'
'-x, -y, -z'
'x-1/2, y, -z-1/2'
'x, -y-1/2, z-1/2'
'-x-1/2, y-1/2, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_adp_type
_atom_site_occupancy
_atom_site_symmetry_multiplicity
_atom_site_calc_flag
_atom_site_refinement_flags
_atom_site_disorder_assembly
_atom_site_disorder_group
Ta1 Ta 0.60234(2) 0.73936(3) 0.234298(15) 0.08061(16) Uani 1 1 d . . .
Ta2 Ta 0.71532(2) 0.87377(2) 0.019606(15) 0.08071(16) Uani 1 1 d . . .
Mo1 Mo 0.56295(4) 0.86223(5) 0.07049(3) 0.0715(2) Uani 1 1 d . . .
Mo2 Mo 0.52188(4) 0.81252(5) 0.14877(3) 0.0696(2) Uani 1 1 d . . .
Mo3 Mo 0.7101(4) 0.7552(5) 0.1248(2) 0.084(3) Uani 0.412(13) 1 d P . .
Mo3A Mo 0.72864(16) 0.7921(3) 0.13971(14) 0.0802(11) Uani 0.588(13) 1 d P . .
O1 O 0.5698(3) 0.8998(3) 0.13166(19) 0.0701(16) Uani 1 1 d . . .
O2 O 0.5494(3) 0.7661(3) 0.0934(2) 0.0773(17) Uani 1 1 d . . .
O3 O 0.6361(3) 0.9390(3) 0.0498(2) 0.0757(17) Uani 1 1 d . . .
O4 O 0.6160(4) 0.8206(4) 0.0136(2) 0.0843(19) Uani 1 1 d . . .
O5 O 0.5461(3) 0.8344(4) 0.2174(2) 0.0784(17) Uani 1 1 d . . .
O6 O 0.6492(3) 0.7718(4) 0.1735(2) 0.086(2) Uani 1 1 d . . .
O7 O 0.5255(3) 0.7145(3) 0.1840(2) 0.0777(18) Uani 1 1 d . . .
O8 O 0.6451(4) 0.6504(4) 0.2312(3) 0.107(2) Uani 1 1 d . . .
O9 O 0.4338(3) 0.8265(4) 0.1471(2) 0.096(2) Uani 1 1 d . . .
O10 O 0.7017(4) 0.8280(3) 0.0838(2) 0.085(2) Uani 1 1 d . . .
O11 O 0.6687(4) 0.7879(5) 0.2696(3) 0.117(3) Uani 1 1 d . . .
O12 O 0.4858(4) 0.8896(4) 0.0476(3) 0.103(2) Uani 1 1 d . . .
O13 O 0.7897(4) 0.9295(5) 0.0399(3) 0.111(3) Uani 1 1 d . . .
O14 O 0.7019(4) 0.9202(4) -0.0364(3) 0.114(3) Uani 1 1 d . . .
O15 O 0.5374(4) 0.7184(4) 0.2805(3) 0.103(2) Uani 1 1 d . . .
O16 O 0.7636(5) 0.7939(4) -0.0023(3) 0.108(3) Uani 1 1 d . . .
O17 O 0.7746(17) 0.7190(18) 0.1317(11) 0.169(17) Uani 0.588(13) 1 d P . .
O18 O 0.7827(12) 0.8502(15) 0.1678(7) 0.170(10) Uani 0.588(13) 1 d P . .
O17A O 0.7031(13) 0.6733(10) 0.1031(9) 0.122(9) Uani 0.412(13) 1 d P . .
O18A O 0.7935(17) 0.765(4) 0.150(2) 0.20(3) Uani 0.412(13) 1 d P . .
C1 C 0.6452(6) 1.0142(5) 0.0628(4) 0.090(3) Uani 1 1 d . . .
C2 C 0.4990(7) 0.6445(7) 0.1740(5) 0.116(4) Uani 1 1 d . . .
C3 C 0.6808(7) 1.0193(7) 0.1095(5) 0.118(4) Uani 1 1 d . . .
C4 C 0.5688(7) 1.0487(6) 0.0621(4) 0.119(4) Uani 1 1 d . . .
C5 C 0.6022(10) 0.7588(8) -0.0135(6) 0.134(6) Uani 1 1 d . . .
C6 C 0.5455(9) 0.8994(9) 0.2440(5) 0.133(5) Uani 1 1 d . . .
C7 C 0.5278(12) 0.6129(9) 0.1312(6) 0.192(9) Uani 1 1 d . . .
C8 C 0.4705(9) 0.7155(10) 0.3043(7) 0.161(7) Uani 1 1 d . . .
C9 C 0.8107(13) 0.7440(10) -0.0207(9) 0.194(10) Uani 1 1 d . . .
C10 C 0.4174(8) 0.6493(10) 0.1717(7) 0.175(8) Uani 1 1 d . . .
C11 C 0.6009(11) 0.9490(10) 0.2311(6) 0.175(7) Uani 1 1 d . . .
C13 C 0.8503(15) 0.7688(14) -0.0568(9) 0.273(17) Uani 1 1 d . . .
C14 C 0.8521(12) 0.9688(14) 0.0562(9) 0.201(9) Uani 1 1 d . . .
C15 C 0.6248(15) 0.6911(11) 0.0086(8) 0.234(12) Uani 1 1 d . . .
C16 C 0.4744(13) 0.7566(15) 0.3472(8) 0.253(13) Uani 1 1 d . . .
C17 C 0.4488(14) 0.6439(15) 0.3127(9) 0.256(13) Uani 1 1 d . . .
C18 C 0.8328(16) 0.6950(16) 0.0074(11) 0.300(17) Uani 1 1 d . . .
C19 C 0.7287(15) 0.8076(16) 0.2988(11) 0.245(12) Uani 1 1 d . . .
C20 C 0.8900(15) 0.986(2) 0.0152(13) 0.35(2) Uani 1 1 d . . .
C21 C 0.8943(15) 0.9182(16) 0.0834(13) 0.32(2) Uani 1 1 d . . .
C24 C 0.530(2) 0.7605(15) -0.0269(12) 0.33(2) Uani 1 1 d . . .
C22 C 0.4746(14) 0.9321(15) 0.2369(10) 0.308(18) Uani 1 1 d . . .
C29 C 0.7824(15) 0.821(3) 0.2798(14) 0.40(4) Uani 1 1 d . . .
C30 C 0.702(3) 0.832(3) 0.3433(12) 0.45(3) Uani 1 1 d . . .
C23 C 0.657(2) 0.993(2) -0.0734(11) 0.285(15) Uiso 1 1 d . . .
C27 C 0.729(3) 0.995(2) -0.0857(18) 0.42(2) Uiso 1 1 d . . .
C28 C 0.6350(18) 0.936(2) -0.0880(12) 0.311(17) Uiso 1 1 d . . .
C12 C 0.7006(15) 0.5920(16) 0.2178(9) 0.227(10) Uiso 1 1 d . . .
C25 C 0.750(2) 0.601(2) 0.2498(17) 0.40(2) Uiso 1 1 d . . .
C26 C 0.6723(19) 0.525(2) 0.2188(11) 0.324(16) Uiso 1 1 d . . .
loop_
_atom_type_symbol
_atom_type_description
_atom_type_scat_dispersion_real
_atom_type_scat_dispersion_imag
_atom_type_scat_source
C C 0.0033 0.0016 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
H H 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
O O 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Mo Mo -1.6832 0.6857 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
Ta Ta -0.7052 6.5227 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
_geom_angle_publ_flag
O8 Ta1 O11 99.7(4) . . ?
O8 Ta1 O15 97.8(3) . . ?
O11 Ta1 O15 98.4(4) . . ?
O8 Ta1 O6 91.9(3) . . ?
O11 Ta1 O6 92.5(3) . . ?
O15 Ta1 O6 163.9(3) . . ?
O8 Ta1 O7 94.0(3) . . ?
O11 Ta1 O7 162.7(3) . . ?
O15 Ta1 O7 90.2(3) . . ?
O6 Ta1 O7 76.3(2) . . ?
O8 Ta1 O5 163.0(3) . . ?
O11 Ta1 O5 93.5(3) . . ?
O15 Ta1 O5 90.7(3) . . ?
O6 Ta1 O5 76.8(3) . . ?
O7 Ta1 O5 71.3(2) . . ?
O8 Ta1 Mo2 123.2(3) . . ?
O11 Ta1 Mo2 122.8(3) . . ?
O15 Ta1 Mo2 109.7(2) . . ?
O6 Ta1 Mo2 54.23(19) . . ?
O7 Ta1 Mo2 39.87(17) . . ?
O5 Ta1 Mo2 39.82(17) . . ?
O13 Ta2 O16 100.8(4) . . ?
O13 Ta2 O14 97.1(4) . . ?
O16 Ta2 O14 97.8(3) . . ?
O13 Ta2 O10 92.1(3) . . ?
O16 Ta2 O10 92.4(3) . . ?
O14 Ta2 O10 164.7(3) . . ?
O13 Ta2 O3 94.7(3) . . ?
O16 Ta2 O3 161.5(3) . . ?
O14 Ta2 O3 90.1(3) . . ?
O10 Ta2 O3 76.9(2) . . ?
O13 Ta2 O4 163.7(3) . . ?
O16 Ta2 O4 91.8(3) . . ?
O14 Ta2 O4 91.4(3) . . ?
O10 Ta2 O4 76.9(3) . . ?
O3 Ta2 O4 71.3(2) . . ?
O13 Ta2 Mo1 124.5(3) . . ?
O16 Ta2 Mo1 122.7(3) . . ?
O14 Ta2 Mo1 108.1(2) . . ?
O10 Ta2 Mo1 56.62(19) . . ?
O3 Ta2 Mo1 38.92(17) . . ?
O4 Ta2 Mo1 39.23(17) . . ?
O12 Mo1 O1 108.4(3) . . ?
O12 Mo1 O2 107.7(3) . . ?
O1 Mo1 O2 91.5(3) . . ?
O12 Mo1 O3 104.6(3) . . ?
O1 Mo1 O3 88.5(2) . . ?
O2 Mo1 O3 145.9(3) . . ?
O12 Mo1 O4 102.3(3) . . ?
O1 Mo1 O4 147.3(3) . . ?
O2 Mo1 O4 89.7(3) . . ?
O3 Mo1 O4 72.9(3) . . ?
O12 Mo1 Mo2 101.5(3) . . ?
O1 Mo1 Mo2 47.93(18) . . ?
O2 Mo1 Mo2 47.21(19) . . ?
O3 Mo1 Mo2 134.67(18) . . ?
O4 Mo1 Mo2 135.50(19) . . ?
O12 Mo1 Ta2 124.6(3) . . ?
O1 Mo1 Ta2 109.96(17) . . ?
O2 Mo1 Ta2 109.75(19) . . ?
O3 Mo1 Ta2 39.82(16) . . ?
O4 Mo1 Ta2 40.14(19) . . ?
Mo2 Mo1 Ta2 133.97(4) . . ?
O9 Mo2 O2 108.4(3) . . ?
O9 Mo2 O1 109.0(3) . . ?
O2 Mo2 O1 92.1(3) . . ?
O9 Mo2 O7 100.4(3) . . ?
O2 Mo2 O7 90.6(3) . . ?
O1 Mo2 O7 147.9(3) . . ?
O9 Mo2 O5 102.3(3) . . ?
O2 Mo2 O5 147.1(3) . . ?
O1 Mo2 O5 88.9(2) . . ?
O7 Mo2 O5 72.1(3) . . ?
O9 Mo2 Mo1 102.5(2) . . ?
O2 Mo2 Mo1 48.04(19) . . ?
O1 Mo2 Mo1 47.74(17) . . ?
O7 Mo2 Mo1 137.38(18) . . ?
O5 Mo2 Mo1 135.25(18) . . ?
O9 Mo2 Ta1 123.6(2) . . ?
O2 Mo2 Ta1 109.61(19) . . ?
O1 Mo2 Ta1 109.64(17) . . ?
O7 Mo2 Ta1 40.27(18) . . ?
O5 Mo2 Ta1 40.45(18) . . ?
Mo1 Mo2 Ta1 133.96(3) . . ?
Mo3A Mo3 O17 87.7(16) . . ?
Mo3A Mo3 O17A 159.0(9) . . ?
O17 Mo3 O17A 71.4(15) . . ?
Mo3A Mo3 O18A 50(2) . . ?
O17 Mo3 O18A 38(2) . . ?
O17A Mo3 O18A 109(2) . . ?
Mo3A Mo3 O10 77.2(5) . . ?
O17 Mo3 O10 121.8(15) . . ?
O17A Mo3 O10 115.4(9) . . ?
O18A Mo3 O10 106.2(18) . . ?
Mo3A Mo3 O6 74.9(5) . . ?
O17 Mo3 O6 120.5(14) . . ?
O17A Mo3 O6 113.4(8) . . ?
O18A Mo3 O6 102.6(19) . . ?
O10 Mo3 O6 109.0(4) . . ?
Mo3 Mo3A O18A 100(3) . . ?
Mo3 Mo3A O17 59.5(13) . . ?
O18A Mo3A O17 41(3) . . ?
Mo3 Mo3A O18 165.8(11) . . ?
O18A Mo3A O18 66(3) . . ?
O17 Mo3A O18 106.4(14) . . ?
Mo3 Mo3A O6 77.3(4) . . ?
O18A Mo3A O6 123(2) . . ?
O17 Mo3A O6 109.9(13) . . ?
O18 Mo3A O6 111.3(8) . . ?
Mo3 Mo3A O10 74.7(4) . . ?
O18A Mo3A O10 126(2) . . ?
O17 Mo3A O10 108.9(12) . . ?
O18 Mo3A O10 111.3(7) . . ?
O6 Mo3A O10 109.0(3) . . ?
Mo3 Mo3A O17A 13.7(6) . . ?
O18A Mo3A O17A 87(3) . . ?
O17 Mo3A O17A 45.9(13) . . ?
O18 Mo3A O17A 152.2(11) . . ?
O6 Mo3A O17A 83.6(5) . . ?
O10 Mo3A O17A 83.7(6) . . ?
Mo1 O1 Mo2 84.3(2) . . ?
Mo2 O2 Mo1 84.7(3) . . ?
C1 O3 Mo1 131.4(6) . . ?
C1 O3 Ta2 125.1(6) . . ?
Mo1 O3 Ta2 101.3(3) . . ?
C5 O4 Mo1 130.9(9) . . ?
C5 O4 Ta2 125.8(8) . . ?
Mo1 O4 Ta2 100.6(3) . . ?
C6 O5 Mo2 132.6(8) . . ?
C6 O5 Ta1 125.6(8) . . ?
Mo2 O5 Ta1 99.7(3) . . ?
Mo3A O6 Mo3 27.8(2) . . ?
Mo3A O6 Ta1 150.3(4) . . ?
Mo3 O6 Ta1 150.7(4) . . ?
C2 O7 Mo2 133.1(7) . . ?
C2 O7 Ta1 125.7(7) . . ?
Mo2 O7 Ta1 99.9(3) . . ?
C12 O8 Ta1 158.8(12) . . ?
Mo3 O10 Mo3A 28.1(2) . . ?
Mo3 O10 Ta2 153.1(4) . . ?
Mo3A O10 Ta2 156.7(4) . . ?
C19 O11 Ta1 165.2(14) . . ?
C14 O13 Ta2 175.7(12) . . ?
Ta2 O14 C23 151.1(11) . . ?
C8 O15 Ta1 158.9(10) . . ?
C9 O16 Ta2 168.4(11) . . ?
O18A O17 Mo3 89(3) . . ?
O18A O17 Mo3A 56(3) . . ?
Mo3 O17 Mo3A 32.8(6) . . ?
O18A O17 O17A 149(3) . . ?
Mo3 O17 O17A 60.7(14) . . ?
Mo3A O17 O17A 93.6(15) . . ?
Mo3A O18 O18A 47.5(12) . . ?
Mo3 O17A O17 47.8(10) . . ?
Mo3 O17A Mo3A 7.3(4) . . ?
O17 O17A Mo3A 40.6(8) . . ?
O17 O18A Mo3A 83(3) . . ?
O17 O18A O18 150(4) . . ?
Mo3A O18A O18 67(2) . . ?
O17 O18A Mo3 54(2) . . ?
Mo3A O18A Mo3 29.9(10) . . ?
O18 O18A Mo3 97(2) . . ?
O3 C1 C3 110.1(9) . . ?
O3 C1 C4 106.2(9) . . ?
C3 C1 C4 113.0(10) . . ?
O7 C2 C7 114.0(11) . . ?
O7 C2 C10 107.8(12) . . ?
C7 C2 C10 110.6(15) . . ?
O4 C5 C24 108.1(15) . . ?
O4 C5 C15 113.3(15) . . ?
C24 C5 C15 115(2) . . ?
O5 C6 C11 113.1(13) . . ?
O5 C6 C22 106.1(14) . . ?
C11 C6 C22 111(2) . . ?
C17 C8 O15 111.8(16) . . ?
C17 C8 C16 111(2) . . ?
O15 C8 C16 110.3(15) . . ?
C18 C9 C13 123(2) . . ?
C18 C9 O16 116(2) . . ?
C13 C9 O16 114.7(17) . . ?
C20 C14 O13 104(2) . . ?
C20 C14 C21 109(3) . . ?
O13 C14 C21 107(2) . . ?
C29 C19 O11 116(3) . . ?
C29 C19 C30 131(4) . . ?
O11 C19 C30 109(3) . . ?
C28 C23 C27 106(4) . . ?
C28 C23 O14 75(3) . . ?
C27 C23 O14 75(3) . . ?
C25 C12 C26 112(4) . . ?
C25 C12 O8 102(3) . . ?
C26 C12 O8 112(3) . . ?
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_distance
_geom_bond_site_symmetry_2
_geom_bond_publ_flag
Ta1 O8 1.839(8) . ?
Ta1 O11 1.850(8) . ?
Ta1 O15 1.855(7) . ?
Ta1 O6 2.065(6) . ?
Ta1 O7 2.106(6) . ?
Ta1 O5 2.113(7) . ?
Ta1 Mo2 3.2106(10) . ?
Ta2 O13 1.836(8) . ?
Ta2 O16 1.851(7) . ?
Ta2 O14 1.859(7) . ?
Ta2 O10 2.065(6) . ?
Ta2 O3 2.110(6) . ?
Ta2 O4 2.120(7) . ?
Ta2 Mo1 3.2323(10) . ?
Mo1 O12 1.675(7) . ?
Mo1 O1 1.913(6) . ?
Mo1 O2 1.921(6) . ?
Mo1 O3 2.071(6) . ?
Mo1 O4 2.080(6) . ?
Mo1 Mo2 2.5728(12) . ?
Mo2 O9 1.679(6) . ?
Mo2 O2 1.896(6) . ?
Mo2 O1 1.919(6) . ?
Mo2 O7 2.089(6) . ?
Mo2 O5 2.086(6) . ?
Mo3 Mo3A 0.882(6) . ?
Mo3 O17 1.40(3) . ?
Mo3 O17A 1.65(2) . ?
Mo3 O18A 1.74(4) . ?
Mo3 O10 1.808(7) . ?
Mo3 O6 1.845(7) . ?
Mo3A O18A 1.36(3) . ?
Mo3A O17 1.63(2) . ?
Mo3A O18 1.691(18) . ?
Mo3A O6 1.827(6) . ?
Mo3A O10 1.827(7) . ?
Mo3A O17A 2.49(2) . ?
O3 C1 1.456(11) . ?
O4 C5 1.415(15) . ?
O5 C6 1.433(15) . ?
O7 C2 1.419(13) . ?
O8 C12 1.55(3) . ?
O11 C19 1.46(2) . ?
O13 C14 1.46(2) . ?
O14 C23 1.92(3) . ?
O15 C8 1.438(15) . ?
O16 C9 1.389(18) . ?
O17 O18A 1.07(6) . ?
O17 O17A 1.79(4) . ?
O18 O18A 1.68(6) . ?
C1 C3 1.515(16) . ?
C1 C4 1.574(15) . ?
C2 C7 1.479(19) . ?
C2 C10 1.539(18) . ?
C5 C24 1.42(3) . ?
C5 C15 1.47(3) . ?
C6 C11 1.44(2) . ?
C6 C22 1.48(3) . ?
C8 C17 1.41(3) . ?
C8 C16 1.46(2) . ?
C9 C18 1.29(3) . ?
C9 C13 1.37(2) . ?
C14 C20 1.42(3) . ?
C14 C21 1.46(3) . ?
C19 C29 1.18(3) . ?
C19 C30 1.46(4) . ?
C23 C28 1.20(4) . ?
C23 C27 1.41(5) . ?
C12 C25 1.33(5) . ?
C12 C26 1.35(4) . ?