Information card for entry 7115201
Preview
| Coordinates | 7115201.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C12 H15 Ga5 N2 O24 P4 |
|---|---|
| Calculated formula | C12 H10 Ga5 N2 O24 P4 |
| Title of publication | Synthesis, crystal structure and 71Ga MAS NMR spectroscopy of a novel gallium phosphatooxalate: [Ga5(OH)2(C10H9N2)(C2O4)(PO4)4]·2H2O |
| Authors of publication | Chen, Ching-Yeh; Chu, Peter P.; Lii, Kwang-Hwa; Lii, Kwang-Hwa |
| Journal of publication | Chemical Communications |
| Year of publication | 1999 |
| Journal issue | 16 |
| Pages of publication | 1473 |
| a | 18.343 ± 0.0002 Å |
| b | 15.9372 ± 0.0004 Å |
| c | 9.1019 ± 0.0002 Å |
| α | 90° |
| β | 90.867 ± 0.001° |
| γ | 90° |
| Cell volume | 2660.51 ± 0.09 Å3 |
| Cell temperature | 293 ± 2 K |
| Ambient diffraction temperature | 293 ± 2 K |
| Number of distinct elements | 6 |
| Space group number | 15 |
| Hermann-Mauguin space group symbol | C 1 2/c 1 |
| Hall space group symbol | -C 2yc |
| Residual factor for all reflections | 0.0682 |
| Residual factor for significantly intense reflections | 0.041 |
| Weighted residual factors for significantly intense reflections | 0.0806 |
| Weighted residual factors for all reflections included in the refinement | 0.0921 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.072 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 180266 (current) | 2016-03-26 | cif/7/11/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 7/11/52. |
7115201.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
7115201.cif |
| 120136 | 2014-07-12 | cif/ Adding structures of 7115201 via cif-deposit CGI script. |
7115201.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.