Information card for entry 8103032
Preview
| Coordinates | 8103032.cif |
|---|
| Common name | Praseodymium orthoscandate perowskite |
|---|---|
| Chemical name | Praseodymium orthoscandate |
| Formula | O3 Pr Sc |
| Calculated formula | O3 Pr Sc |
| Title of publication | Refinement of the crystal structure of praseodymium orthoscandate, PrScO3 |
| Authors of publication | Thorsten M. Gesing; Reinhard Uecker; J.-Christian Buhl |
| Journal of publication | Zeitschrift für Kristallographie - New Crystal Structures |
| Year of publication | 2009 |
| Journal volume | 224 |
| Journal issue | 3 |
| Pages of publication | 365 |
| a | 5.7804 ± 0.0012 Å |
| b | 8.025 ± 0.002 Å |
| c | 5.6077 ± 0.0011 Å |
| α | 90° |
| β | 90° |
| γ | 90° |
| Cell volume | 260.13 ± 0.1 Å3 |
| Cell temperature | 298 K |
| Ambient diffraction temperature | 298 K |
| Number of distinct elements | 3 |
| Space group number | 62 |
| Hermann-Mauguin space group symbol | P n m a |
| Hall space group symbol | -P 2ac 2n |
| Residual factor for all reflections | 0.0255 |
| Residual factor for significantly intense reflections | 0.0246 |
| Weighted residual factors for all reflections | 0.0606 |
| Weighted residual factors for significantly intense reflections | 0.06 |
| Goodness-of-fit parameter for all reflections | 1.112 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.121 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 176728 (current) | 2016-02-18 | cif/ (antanas@echidna.ibt.lt) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in range 8. |
8103032.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
8103032.cif |
| 35911 | 2012-02-28 | cif/ Reorganising ranges 1, 3, 5, 6 and 8 into a prefix-directory tree. |
8103032.cif |
| 18059 | 2011-04-15 | cif/8/ Correcting temperature value in 8103032.cif using the Adriana's cif_fix_values program. |
8103032.cif |
| 18058 | 2011-04-15 | cif/8/ Correcting syntax in 8103032.cif. |
8103032.cif |
| 16262 | 2011-03-21 | cif/8/ Deleting unicode symbols near the numeric temperature values. |
8103032.cif |
| 13771 | 2011-03-06 | ../uploads/cif-deposit/cod/cif Adding structures of 8103032 via cif-deposit CGI script. |
8103032.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.