Information card for entry 8103054
Preview
| Coordinates | 8103054.cif |
|---|
| Formula | B8 Ca6.6 Cd1.4 O20 |
|---|---|
| Calculated formula | B8 Ca6.6 Cd1.4 O20 |
| Title of publication | Crystal structure of calcium cadmium borate, Ca6.6Cd1.4(B2O5)4 |
| Authors of publication | Zhi-Wei Jiao; De-Zhong Shen; Ru-Ji Wang; Guang-Qiu Shen; Xiao-Qing Wang |
| Journal of publication | Zeitschrift für Kristallographie - New Crystal Structures |
| Year of publication | 2010 |
| Journal volume | 225 |
| Journal issue | 4 |
| Pages of publication | 623 |
| a | 7.1306 ± 0.0018 Å |
| b | 5.1843 ± 0.0007 Å |
| c | 11.484 ± 0.003 Å |
| α | 90° |
| β | 92.57 ± 0.03° |
| γ | 90° |
| Cell volume | 424.1 ± 0.16 Å3 |
| Cell temperature | 295 ± 2 K |
| Ambient diffraction temperature | 295 ± 2 K |
| Number of distinct elements | 4 |
| Space group number | 14 |
| Hermann-Mauguin space group symbol | P 1 21/c 1 |
| Hall space group symbol | -P 2ybc |
| Residual factor for all reflections | 0.0476 |
| Residual factor for significantly intense reflections | 0.0472 |
| Weighted residual factors for significantly intense reflections | 0.1156 |
| Weighted residual factors for all reflections included in the refinement | 0.1158 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.113 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 176466 (current) | 2016-02-16 | cif/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in range 8. |
8103054.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
8103054.cif |
| 35911 | 2012-02-28 | cif/ Reorganising ranges 1, 3, 5, 6 and 8 into a prefix-directory tree. |
8103054.cif |
| 13793 | 2011-03-06 | ../uploads/cif-deposit/cod/cif Adding structures of 8103054 via cif-deposit CGI script. |
8103054.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.