Information card for entry 7205733
Preview
Coordinates | 7205733.cif |
---|---|
Original paper (by DOI) | HTML |
Formula | C16 H14 Dy2 O14 |
---|---|
Calculated formula | C16 H14 Dy2 O14 |
Title of publication | A novel family of 3D photoluminescent lanthanide‒bta‒flexible MOFs constructed from 1,2,4,5-benzenetetracarboxylic acid and different spanning of dicarboxylate acid ligands |
Authors of publication | Hou, Ke-Ling; Bai, Feng-Ying; Xing, Yong-Heng; Wang, Jian-Ling; Shi, Zhan |
Journal of publication | CrystEngComm |
Year of publication | 2011 |
Journal volume | 13 |
Journal issue | 11 |
Pages of publication | 3884 |
a | 7.7659 ± 0.0007 Å |
b | 7.2009 ± 0.0006 Å |
c | 17.3199 ± 0.0015 Å |
α | 90° |
β | 91.452 ± 0.001° |
γ | 90° |
Cell volume | 968.24 ± 0.15 Å3 |
Cell temperature | 273 ± 2 K |
Ambient diffraction temperature | 273 ± 2 K |
Number of distinct elements | 4 |
Space group number | 14 |
Hermann-Mauguin space group symbol | P 1 21/n 1 |
Hall space group symbol | -P 2yn |
Residual factor for all reflections | 0.0225 |
Residual factor for significantly intense reflections | 0.019 |
Weighted residual factors for significantly intense reflections | 0.0472 |
Weighted residual factors for all reflections included in the refinement | 0.0491 |
Goodness-of-fit parameter for all reflections included in the refinement | 1.084 |
Diffraction radiation wavelength | 0.71073 Å |
Diffraction radiation type | MoKα |
Has coordinates | Yes |
Has disorder | No |
Has Fobs | No |
Revision | Date | Message | Files |
---|---|---|---|
180388 (current) | 2016-03-26 | cif/7/20/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 7/20/57. |
7205733.cif |
130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
7205733.cif |
120112 | 2014-07-12 | Adding DOIs to range 7 structures. | 7205733.cif |
35909 | 2012-02-26 | cif/7/: reorganising range 7 into a prefix-directory tree. | 7205733.cif |
20998 | 2011-06-21 | ../uploads/cif-deposit/cod/cif Adding structures of 7205722, 7205723, 7205724, 7205725, 7205726, 7205727, 7205728, 7205729, 7205730, 7205731, 7205732, 7205733 via cif-deposit CGI script. |
7205733.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.