Crystallography Open Database

Information card for entry 4301569

Preview

Coordinates	4301569.cif
Original paper (by DOI)	HTML

Structure parameters

Common name	PCN-17 (Y)
Formula	C72 H62 N8 O31 S6 Y4
Calculated formula	C72 H56 N8 O31 S6 Y4
Title of publication	Microporous Lanthanide Metal-Organic Frameworks Containing Coordinatively Linked Interpenetration: Syntheses, Gas Adsorption Studies, Thermal Stability Analysis, and Photoluminescence Investigation
Authors of publication	Shengqian Ma; Daqiang Yuan; Xi-Sen Wang; Hong-Cai Zhou
Journal of publication	Inorganic Chemistry
Year of publication	2009
Journal volume	48
Pages of publication	2072 - 2077
a	26.311 ± 0.003 Å
b	26.311 ± 0.003 Å
c	26.311 ± 0.003 Å
α	90°
β	90°
γ	90°
Cell volume	18214 ± 4 Å³
Cell temperature	213 ± 2 K
Ambient diffraction temperature	213 ± 2 K
Number of distinct elements	6
Space group number	229
Hermann-Mauguin space group symbol	I m -3 m
Hall space group symbol	-I 4 2 3
Residual factor for all reflections	0.1104
Residual factor for significantly intense reflections	0.0921
Weighted residual factors for significantly intense reflections	0.2555
Weighted residual factors for all reflections included in the refinement	0.2707
Goodness-of-fit parameter for all reflections included in the refinement	1.107
Diffraction radiation wavelength	0.71073 Å
Diffraction radiation type	MoKα
Has coordinates	Yes
Has disorder	No
Has F_obs	No

Version history

Revision	Date	Message	Files
179053 (current)	2016-03-22	cif/4/30/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/30/15.	4301569.cif
130086	2015-01-23	cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ \| xargs -i sh -c 'cif_fix_values {} \ \| cif_filter --add-cif-header {} \ \| sponge {}'	4301569.cif
120081	2014-07-12	Adding DOIs to range 4/30 structures.	4301569.cif
34330	2012-02-24	cif/4/ Reorganising CIF range 4 into a prefix tree.	4301569.cif
17004	2011-03-31	cif/ Commiting CIFs, that were updated with the 'cif_fix_values' script, using options '--fix-misspelled replacement_values.lst', '--fix-temperature' and '--fix-enums' with built-in table of enum values. The following cmd was used: > (set -x; find ? -name \*.cif \| sort \| xargs -i sh -c 'if !( > cif_fix_values --fix-misspelled ~/../inputs/replacament_values.lst {} \| > cif_filter --add-cif-header {} \| > sponge {} ) 2>&1 \| grep NOTE; then svn revert {}; > fi' ) &	4301569.cif
5312	2011-01-03	cif/ Adding files, updated with the 'cif_fix_enum' program and the cif_core.dic dictionary. The enumerator values were fixed, mostly incorrect case, but also some values that had extra underscores, dashes or spaces. Unfortunately, 22 had non-ASCII characters with the 8-th bit set, and these got incorrectly interpreted as latin1 characters and converted to their UTF8 equivalents by Perl. To fix the structures, however, they need to be redeposited from the original files with the new CIFParser/cif_filter version.	4301569.cif
1054	2010-03-28	cif/4/ Adding data extracted in Inorg-Chem-2009_01-10/ processing.	4301569.cif