Information card for entry 7215362
Preview
| Coordinates | 7215362.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C22 H30 Co2 N2 O13 |
|---|---|
| Calculated formula | C22 H26 Co2 N2 O12 |
| Title of publication | Three three-dimensional anionic metal‒organic frameworks with (4,8)-connected alb topology constructed from a semi-rigid ligand and polynuclear metal clusters |
| Authors of publication | Su, Shengqun; Qin, Chao; Song, Shuyan; Guo, Zhiyong; Deng, Ruiping; Chen, Wan; Song, Xuezhi; Wang, Song; Li, Guanghua; Zhang, Hongjie |
| Journal of publication | CrystEngComm |
| Year of publication | 2011 |
| Journal volume | 13 |
| Journal issue | 20 |
| Pages of publication | 6057 |
| a | 11.066 ± 0.0005 Å |
| b | 13.8214 ± 0.0006 Å |
| c | 16.8387 ± 0.0007 Å |
| α | 90° |
| β | 103.31 ± 0.001° |
| γ | 90° |
| Cell volume | 2506.26 ± 0.19 Å3 |
| Cell temperature | 185 ± 2 K |
| Ambient diffraction temperature | 185 ± 2 K |
| Number of distinct elements | 5 |
| Space group number | 14 |
| Hermann-Mauguin space group symbol | P 1 21/n 1 |
| Hall space group symbol | -P 2yn |
| Residual factor for all reflections | 0.0506 |
| Residual factor for significantly intense reflections | 0.0376 |
| Weighted residual factors for significantly intense reflections | 0.0945 |
| Weighted residual factors for all reflections included in the refinement | 0.1017 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.051 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 180484 (current) | 2016-03-26 | cif/7/21/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 7/21/53. |
7215362.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
7215362.cif |
| 111926 | 2014-04-28 | cif/ Adding structures of 7215362, 7215363, 7215364 via cif-deposit CGI script. |
7215362.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.