Information card for entry 4077451
Preview
| Coordinates | 4077451.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C61 H91 N5 Nd2 O12 |
|---|---|
| Calculated formula | C62.18 H86 N4 Nd2 O12 |
| Title of publication | Lanthanide Carboxylate Precursors for Diene Polymerization Catalysis: Syntheses, Structures, and Reactivity with Et2AlCl |
| Authors of publication | Evans, William J.; Giarikos, Dimitrios G.; Ziller, Joseph W. |
| Journal of publication | Organometallics |
| Year of publication | 2001 |
| Journal volume | 20 |
| Journal issue | 26 |
| Pages of publication | 5751 |
| a | 11.4336 ± 0.0008 Å |
| b | 16.182 ± 0.0012 Å |
| c | 18.0028 ± 0.0013 Å |
| α | 90° |
| β | 101.597 ± 0.001° |
| γ | 90° |
| Cell volume | 3262.9 ± 0.4 Å3 |
| Cell temperature | 158 ± 2 K |
| Ambient diffraction temperature | 158 ± 2 K |
| Number of distinct elements | 5 |
| Space group number | 14 |
| Hermann-Mauguin space group symbol | P 1 21/n 1 |
| Hall space group symbol | -P 2yn |
| Residual factor for all reflections | 0.0541 |
| Residual factor for significantly intense reflections | 0.0344 |
| Weighted residual factors for significantly intense reflections | 0.0704 |
| Weighted residual factors for all reflections included in the refinement | 0.0792 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.026 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | Yes |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 178663 (current) | 2016-03-21 | cif/4/07/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/07/74. |
4077451.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4077451.cif |
| 91935 | 2013-12-29 | cod/ (saulius@koala.ibt.lt) Adding DOIs that could be assigned unambiguously to the rest of COD CIFs. |
4077451.cif |
| 54353 | 2012-04-24 | cif/ Adding structures of 4077451, 4077452, 4077453, 4077454 via cif-deposit CGI script. |
4077451.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.