Crystallography Open Database

Information card for entry 4308030

Preview

Coordinates	4308030.cif
Original paper (by DOI)	HTML

Structure parameters

Common name	none
Formula	C50 H27 Cd3 N6 O14
Calculated formula	C50 H24 Cd3 N6 O14
Title of publication	Construction of Robust Open Metal-Organic Frameworks with Chiral Channels and Permanent Porosity
Authors of publication	Daofeng Sun; Yanxiong Ke; David J. Collins; Gary A. Lorigan; Hong-Cai Zhou
Journal of publication	Inorganic Chemistry
Year of publication	2007
Journal volume	46
Pages of publication	2725 - 2734
a	18.0494 ± 0.0004 Å
b	18.0494 ± 0.0004 Å
c	27.17 ± 0.0013 Å
α	90°
β	90°
γ	90°
Cell volume	8851.5 ± 0.5 Å³
Cell temperature	213 ± 2 K
Ambient diffraction temperature	213 ± 2 K
Number of distinct elements	5
Space group number	91
Hermann-Mauguin space group symbol	P 41 2 2
Hall space group symbol	P 4w 2c
Residual factor for all reflections	0.0749
Residual factor for significantly intense reflections	0.0631
Weighted residual factors for significantly intense reflections	0.1837
Weighted residual factors for all reflections included in the refinement	0.2007
Goodness-of-fit parameter for all reflections included in the refinement	1.185
Diffraction radiation wavelength	0.71073 Å
Diffraction radiation type	MoKα
Has coordinates	Yes
Has disorder	No
Has F_obs	No

Version history

Revision	Date	Message	Files
179118 (current)	2016-03-23	cif/4/30/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/30/80.	4308030.cif
130086	2015-01-23	cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ \| xargs -i sh -c 'cif_fix_values {} \ \| cif_filter --add-cif-header {} \ \| sponge {}'	4308030.cif
120081	2014-07-12	Adding DOIs to range 4/30 structures.	4308030.cif
34330	2012-02-24	cif/4/ Reorganising CIF range 4 into a prefix tree.	4308030.cif
17004	2011-03-31	cif/ Commiting CIFs, that were updated with the 'cif_fix_values' script, using options '--fix-misspelled replacement_values.lst', '--fix-temperature' and '--fix-enums' with built-in table of enum values. The following cmd was used: > (set -x; find ? -name \*.cif \| sort \| xargs -i sh -c 'if !( > cif_fix_values --fix-misspelled ~/../inputs/replacament_values.lst {} \| > cif_filter --add-cif-header {} \| > sponge {} ) 2>&1 \| grep NOTE; then svn revert {}; > fi' ) &	4308030.cif
5312	2011-01-03	cif/ Adding files, updated with the 'cif_fix_enum' program and the cif_core.dic dictionary. The enumerator values were fixed, mostly incorrect case, but also some values that had extra underscores, dashes or spaces. Unfortunately, 22 had non-ASCII characters with the 8-th bit set, and these got incorrectly interpreted as latin1 characters and converted to their UTF8 equivalents by Perl. To fix the structures, however, they need to be redeposited from the original files with the new CIFParser/cif_filter version.	4308030.cif
1194	2010-06-06	cif/4/ Adding data from Inorg-Chem-2007_01-13/ processing directory.	4308030.cif