Information card for entry 4339494
Preview
| Coordinates | 4339494.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | In3 Sr Zn |
|---|---|
| Calculated formula | In3 Sr Zn |
| Title of publication | Syntheses and structures of new phases AeMxIn(4-x) (Ae = Sr, Ba; M = Mg, Zn): size effects and site preferences in BaAl4-type structures. |
| Authors of publication | Li, Bin; Corbett, John D. |
| Journal of publication | Inorganic chemistry |
| Year of publication | 2007 |
| Journal volume | 46 |
| Journal issue | 21 |
| Pages of publication | 8812 - 8818 |
| a | 4.627 ± 0.001 Å |
| b | 4.627 ± 0.001 Å |
| c | 12.098 ± 0.005 Å |
| α | 90° |
| β | 90° |
| γ | 90° |
| Cell volume | 259.01 ± 0.13 Å3 |
| Cell temperature | 293 ± 2 K |
| Ambient diffraction temperature | 293 ± 2 K |
| Number of distinct elements | 3 |
| Space group number | 139 |
| Hermann-Mauguin space group symbol | I 4/m m m |
| Hall space group symbol | -I 4 2 |
| Residual factor for all reflections | 0.0228 |
| Residual factor for significantly intense reflections | 0.0228 |
| Weighted residual factors for significantly intense reflections | 0.0678 |
| Weighted residual factors for all reflections included in the refinement | 0.0678 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.016 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 179497 (current) | 2016-03-23 | cif/4/33/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/33/94. |
4339494.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4339494.cif |
| 117353 | 2014-06-14 | cif/ Adding structures of 4339488, 4339489, 4339490, 4339491, 4339492, 4339493, 4339494 via cif-deposit CGI script. |
4339494.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.