Information card for entry 4502152
Preview
| Coordinates | 4502152.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C33 H24 Cd2 O14 |
|---|---|
| Calculated formula | C33 H24 Cd2 O14 |
| Title of publication | Metal−Organic Framework Isomers with Diamondoid Networks Constructed of a Semirigid Tetrahedral Linker |
| Authors of publication | Tian, Jian; Motkuri, Radha Kishan; Thallapally, Praveen K.; McGrail, B. Peter |
| Journal of publication | Crystal Growth & Design |
| Year of publication | 2010 |
| Journal volume | 10 |
| Journal issue | 12 |
| Pages of publication | 5327 |
| a | 13.346 ± 0.0011 Å |
| b | 16.1864 ± 0.0013 Å |
| c | 17.7807 ± 0.0015 Å |
| α | 112.598 ± 0.003° |
| β | 107.375 ± 0.003° |
| γ | 97.625 ± 0.003° |
| Cell volume | 3248.1 ± 0.5 Å3 |
| Cell temperature | 100 ± 2 K |
| Ambient diffraction temperature | 100 ± 2 K |
| Number of distinct elements | 4 |
| Space group number | 2 |
| Hermann-Mauguin space group symbol | P -1 |
| Hall space group symbol | -P 1 |
| Residual factor for all reflections | 0.1053 |
| Residual factor for significantly intense reflections | 0.0787 |
| Weighted residual factors for significantly intense reflections | 0.2219 |
| Weighted residual factors for all reflections included in the refinement | 0.2485 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.189 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 179552 (current) | 2016-03-24 | cif/4/50/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/50/21. |
4502152.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4502152.cif |
| 91935 | 2013-12-29 | cod/ (saulius@koala.ibt.lt) Adding DOIs that could be assigned unambiguously to the rest of COD CIFs. |
4502152.cif |
| 36270 | 2012-03-01 | ../uploads/cif-deposit/cod/cif Adding structures of 4502152 via cif-deposit CGI script. |
4502152.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.