Information card for entry 4503205
Preview
| Coordinates | 4503205.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C44 H31 N2 O17 Pr Zn2 |
|---|---|
| Calculated formula | C44 H31 N2 O17 Pr Zn2 |
| Title of publication | Synthesis and Characterization of Three-Dimensional 3d−3d and 3d−4f Heterometallic Coordination Polymers with High Thermal Stability |
| Authors of publication | Ren, Peng; Shi, Wei; Cheng, Peng |
| Journal of publication | Crystal Growth & Design |
| Year of publication | 2008 |
| Journal volume | 8 |
| Journal issue | 4 |
| Pages of publication | 1097 |
| a | 10.4903 ± 0.0013 Å |
| b | 18.331 ± 0.002 Å |
| c | 22.282 ± 0.003 Å |
| α | 90° |
| β | 92.231 ± 0.002° |
| γ | 90° |
| Cell volume | 4281.5 ± 0.9 Å3 |
| Cell temperature | 294 ± 2 K |
| Ambient diffraction temperature | 294 ± 2 K |
| Number of distinct elements | 6 |
| Space group number | 14 |
| Hermann-Mauguin space group symbol | P 1 21/c 1 |
| Hall space group symbol | -P 2ybc |
| Residual factor for all reflections | 0.0764 |
| Residual factor for significantly intense reflections | 0.0393 |
| Weighted residual factors for significantly intense reflections | 0.0729 |
| Weighted residual factors for all reflections included in the refinement | 0.0857 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.003 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 179563 (current) | 2016-03-24 | cif/4/50/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/50/32. |
4503205.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4503205.cif |
| 120110 | 2014-07-12 | Adding DOIs to range 4/50 structures. | 4503205.cif |
| 41410 | 2012-03-13 | ../uploads/cif-deposit/cod/cif Adding structures of 4503205 via cif-deposit CGI script. |
4503205.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.