Information card for entry 4504238
Preview
| Coordinates | 4504238.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Formula | C18 H24 Cu4 N4 O16 |
|---|---|
| Calculated formula | C18 H24 Cu4 N4 O16 |
| Title of publication | Construction of a Three-fold Parallel Interpenetration Network and Bilayer Structure Based on Copper(II) and Trimesic Acid |
| Authors of publication | Chen, Wen-Xian; Wu, Shu-Ting; Long, La-Sheng; Huang, Rong-Bin; Zheng, Lan-Sun |
| Journal of publication | Crystal Growth & Design |
| Year of publication | 2007 |
| Journal volume | 7 |
| Journal issue | 6 |
| Pages of publication | 1171 |
| a | 18.887 ± 0.004 Å |
| b | 10.761 ± 0.002 Å |
| c | 14.488 ± 0.003 Å |
| α | 90° |
| β | 126.1 ± 0.003° |
| γ | 90° |
| Cell volume | 2379.2 ± 0.8 Å3 |
| Cell temperature | 123 ± 2 K |
| Ambient diffraction temperature | 123 ± 2 K |
| Number of distinct elements | 5 |
| Space group number | 15 |
| Hermann-Mauguin space group symbol | C 1 2/c 1 |
| Hall space group symbol | -C 2yc |
| Residual factor for all reflections | 0.0268 |
| Residual factor for significantly intense reflections | 0.0257 |
| Weighted residual factors for significantly intense reflections | 0.0692 |
| Weighted residual factors for all reflections included in the refinement | 0.0699 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.076 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 179577 (current) | 2016-03-24 | cif/4/50/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in subrange 4/50/42. |
4504238.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
4504238.cif |
| 120110 | 2014-07-12 | Adding DOIs to range 4/50 structures. | 4504238.cif |
| 44984 | 2012-03-20 | ../uploads/cif-deposit/cod/cif Adding structures of 4504238 via cif-deposit CGI script. |
4504238.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.