Information card for entry 7014371
Preview
| Coordinates | 7014371.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Common name | Neodymium Silicon Aluminum Oxynitride |
|---|---|
| Chemical name | Neodymium Silicon Aluminum Oxynitride |
| Formula | Al1.4 N9.6 Nd O0.4 Si5.6 |
| Calculated formula | Al1.4 N9.6 Nd O0.4 Si5.6 |
| Title of publication | Crystal structure of NdSi(6-z)Al(1+z)O(z)N(10-z) (z = 0.4) determined by single-crystal X-ray diffraction. |
| Authors of publication | Huang, Saifang; Huang, Zhaohui; Liu, Yan-gai; Fang, Minghao |
| Journal of publication | Dalton transactions (Cambridge, England : 2003) |
| Year of publication | 2011 |
| Journal volume | 40 |
| Journal issue | 6 |
| Pages of publication | 1261 - 1266 |
| a | 9.306 ± 0.0006 Å |
| b | 9.7224 ± 0.0006 Å |
| c | 8.8777 ± 0.0005 Å |
| α | 90° |
| β | 90° |
| γ | 90° |
| Cell volume | 803.22 ± 0.08 Å3 |
| Cell temperature | 293 ± 2 K |
| Ambient diffraction temperature | 293 ± 2 K |
| Number of distinct elements | 5 |
| Space group number | 60 |
| Hermann-Mauguin space group symbol | P b c n |
| Hall space group symbol | -P 2n 2ab |
| Residual factor for all reflections | 0.0297 |
| Residual factor for significantly intense reflections | 0.0289 |
| Weighted residual factors for significantly intense reflections | 0.0734 |
| Weighted residual factors for all reflections included in the refinement | 0.0739 |
| Goodness-of-fit parameter for all reflections included in the refinement | 1.031 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | Yes |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 176453 (current) | 2016-02-16 | cif/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries in range 7. |
7014371.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
7014371.cif |
| 120112 | 2014-07-12 | Adding DOIs to range 7 structures. | 7014371.cif |
| 35909 | 2012-02-26 | cif/7/: reorganising range 7 into a prefix-directory tree. | 7014371.cif |
| 14738 | 2011-03-11 | ../uploads/cif-deposit/cod/cif Adding structures of 7014371 via cif-deposit CGI script. |
7014371.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.