Information card for entry 7026500
Preview
| Coordinates | 7026500.cif |
|---|---|
| Original paper (by DOI) | HTML |
| Common name | none |
|---|---|
| Formula | K O12 Sb3 Zn4 |
| Calculated formula | K O12 Sb3 Zn4 |
| Title of publication | KZn(4)SbO(7) and KZn(4)Sb(3)O(12): syntheses, structures and photophysics of Sb(5+) control materials. |
| Authors of publication | Yang, Song-Lin; Cheng, Wen-Dan; Zhang, Hao; Lin, Chen-Sheng; Zhang, Wei-Long; He, Zhang-Zhen |
| Journal of publication | Dalton transactions (Cambridge, England : 2003) |
| Year of publication | 2010 |
| Journal volume | 39 |
| Journal issue | 40 |
| Pages of publication | 9547 - 9553 |
| a | 10.867 ± 0.009 Å |
| b | 10.867 ± 0.009 Å |
| c | 7.301 ± 0.008 Å |
| α | 90° |
| β | 90° |
| γ | 120° |
| Cell volume | 746.7 ± 1.2 Å3 |
| Cell temperature | 293 ± 2 K |
| Ambient diffraction temperature | 293 ± 2 K |
| Number of distinct elements | 4 |
| Space group number | 146 |
| Hermann-Mauguin space group symbol | R 3 :H |
| Hall space group symbol | R 3 |
| Residual factor for all reflections | 0.0199 |
| Residual factor for significantly intense reflections | 0.0192 |
| Weighted residual factors for significantly intense reflections | 0.0412 |
| Weighted residual factors for all reflections included in the refinement | 0.0414 |
| Goodness-of-fit parameter for all reflections included in the refinement | 0.918 |
| Diffraction radiation wavelength | 0.71073 Å |
| Diffraction radiation type | MoKα |
| Has coordinates | Yes |
| Has disorder | No |
| Has Fobs | No |
| Revision | Date | Message | Files |
|---|---|---|---|
| 176432 (current) | 2016-02-14 | cif/ (antanas@kurmis) Replacing _[local]_cod_* tags with their equivalents from the COD CIF dictionary in multiple entries. |
7026500.cif |
| 130086 | 2015-01-23 | cod/ (robertas@burundukas) The 'cif_fix_values' program was applied to CIFs that have generated the validation messages containing tag '_exptl_crystal_density_meas'. 16946 CIFs had a values that were perceived as 'not measured' and they were changed to '?'. The total of 17089 CIFs was changed. Those that were not corrected by 'cif_fix_values' were reformatted by the parser (e.g. a doi tag was moved to another place). The processing command was: mysql -u cod_reader -h www.crystallography.net cod -e \ 'select distinct codid from validation \ where message like \ "%tag%_exptl_crystal_density_meas'\''%"' -NB \ | xargs -i sh -c 'cif_fix_values {} \ | cif_filter --add-cif-header {} \ | sponge {}' |
7026500.cif |
| 93518 | 2014-01-13 | cif/ Adding structures of 7026499, 7026500 via cif-deposit CGI script. |
7026500.cif |
All data in the COD and the database itself are dedicated to the
public domain and licensed under the
CC0
License
.
Users of the data should acknowledge the original authors of the
structural data.